Overview

Tpcm 900 is a high performance, non-electrically conductive phase change material. At 50°C, Tpcm 900 begins to soften and flow, filling the microscopic irregularities of both the thermal solution and the component's surfaces, thereby reducing thermal resistance.

 

Tpcm 900 is a flexible solid at room temperature and freestanding without reinforcing components that reduce thermal performance.

Tpcm 900 shows no thermal performance degradation after 1,000 hours @130°C, or after 500 cycles, from -25°C to 125°C. The material softens and does not fully change state resulting in minimal migration (pump out) at operating temperatures (see viscosity curve).

 

Tpcm 900 is supplied in rolls with top tabbed liners for easy manual or large volume automatic application. Individually die cut parts can also be supplied.

Standard Thicknesses: 0.005" (0.13mm) 0.010" (0.25mm) 0.020" (0.51mm) Consult the factory for alternate thicknesses Standard Sheet Sizes: 9" x 9" (229mm x 229mm) Tpcm™ 900 sheets are supplied with a white release paper and a bottom liner. Tpcm™ 900 is available in rolls with an extended tab liner or individual die cut shapes. Pressure Sensitive Adhesive: Pressure sensitive adhesive is not applicable for Tpcm™ products. Reinforcement: No reinforcement is necessary.

Specifications

Applications
• High frequency microprocessors
• Notebook and desktop PCs
• Computer servers
• DC/DC converts
• Memory modules
• Cache chips
• IGBTs
Burn In Temperature
70ºC for 5 minutes
Color
Yellow
Construction and Composition
Non-reinforced boron nitride filled film
Datasheet ID
3001233
Dielectric Constant Range
1MHz 3.1, Test Method, ASTM D150
Operating Temperature
- 25C to 125C
Operating Temperature Range (°C)
- 25 to 125
Other
Phase Change Softening Range : 50 to 70
Product Testing Procedures
href="http://www.lairdtech.com/pdfs/Compression2.pdf">Compression/ Deflection href="http://www.lairdtech.com/pdfs/Density.pdf.pdf">Density href="http://www.lairdtech.com/pdfs/Hardness.pdf.pdf">Hardness href="http://www.lairdtech.com/pdfs/Outgassing.pdf.pdf">Outgassing href="http://www.lairdtech.com/pdfs/ThermalResistance.pdf">Thermal Resistance href="http://www.lairdtech.com/pdfs/ThermalConductivity.pdf.pdf">Thermal Conductivity href="http://www.lairdtech.com/pdfs/DiecuttingQA.pdf.pdf">Die Cutting Questions and Answers
Sheet Sizes (inches)
9 x 9
Sheet Sizes (mm)
229 x 229
Shelf Life
1 year
Temperature - Operating (Max Celsius)
125
Temperature - Operating (Min Celsius)
-25
Temperature Range
-25 to 125C
Test Method - Color
Visual
Test Method - Thermal Conductivity
ASTM D5470 (modified)
Thermal Conductivity (W/mK)
2.23
Thermal Resistance (°C-in²/W)
0.083-0.095 (50psi)
Thickness Max (mm)
0.5
Thickness Min (mm)
0.25
Thickness Tolerance (inches)
±0.001
Thickness Tolerance (mm)
±0.025
Volume Resistivity
Volume Resistivity Del 2, Volume Resistivity, ASTM D257

Documentation

File Type Last Updated
THR-DS-Tpcm 900 0910.pdf Datasheet 11-21-18
SDS China Chinese (Simplified) - Tpcm 900 Series(935396).pdf Documentation 11-21-18
SDS EU EU English - Tpcm 900 Series(935396).pdf Documentation 11-21-18
SDS US - Tpcm 900 Series(935396).pdf Documentation 11-21-18